Anti-Skid HDPE Textured Geomembrane For Enhanced Stability On Steep Slopes
Product Introduction
As a kind of geotechnical material with special surface structure, the design of cylindrical rough surface geomembrane aims to improve its anti-skid performance and adhesion to soil or other materials.
Product Properties
1. High coefficient of friction: The column point design significantly increases the friction coefficient of the geomembrane, giving it better stability on steep or vertical slopes.
2. Good impermeable performance: Inherited the excellent impermeable characteristics of HDPE geomemofilm, effectively preventing the penetration of water and pollutants.
3. Enhanced adhesion: The column point structure improves the adhesion of the geomembrane to the soil, helping to prevent sliding of the geomembrane on slopes.
4. Chemical resistance: It has good resistance to most chemical substances and is suitable for use in a variety of environments.
5. Resistance to environmental stress cracking: It can remain stable in harsh environments and is not easy to crack.
6. Temperature adaptability: can be used in a wide temperature range, with good heat resistance and cold resistance.
Product Application
1. Steep slope seepage prevention project: column point rough surface geomembrane is especially suitable for steep slope seepage prevention project, improve the stability of the project.
2. Vertical impermeability: In vertical or near-vertical impermeability projects, the column point design helps to keep the geomembrane fixed.
3. Dam reinforcement: used for dam reinforcement engineering, improve the stability of the dam and anti-seepage performance.
4. Landfill: It is used in the slope anti-slip and anti-seepage of landfill and sealed field to prevent pollutants from penetrating into the environment.
Products series
Single textured geomembrane, double-wall textured geomembrane.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width: 4m~8m
* Roll length: 50m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Textured HDPE Geomembrane For Landfill (GB/T 17643-2011(GH-2T1,GH-2T2))
| Serial Number |
Project |
Index |
| Thickness(mm) |
0.75 |
1.00 |
1.25 |
1.50 |
2.00 |
2.50 |
3.00 |
| 1 |
Density (g/c㎡,≥) |
≥0.940 |
| 2 |
Textured Highth (mm) |
≥0.25 |
| 3 |
Yield Strength (N/mm,LD/TD) |
≥11 |
≥15 |
≥18 |
≥22 |
≥29 |
≥37 |
≥44 |
| 4 |
Breaking Strength (N/mm,LD/TD) |
≥8 |
≥10 |
≥13 |
≥16 |
≥21 |
≥26 |
≥32 |
| 5 |
Yeild Elongation Rate (%) |
≥12 |
| 6 |
Breaking Elongation Rate (%) |
≥100 |
| 7 |
Rectangular Tear Strength (N) |
≥93 |
≥125 |
≥160 |
≥190 |
≥250 |
≥315 |
≥375 |
| 8 |
Puncture Strength (N) |
≥200 |
≥270 |
≥335 |
≥400 |
≥535 |
≥670 |
≥800 |
| 9 |
Tensile Load Stress Cracking (Notch Constant Load Tensle Method) h |
≥300 |
| 10 |
Carbon Black Content(Rang) (%) |
2.0~3.0 |
| 11 |
Carbon Black Dispersion |
There is not more than one grade 3 in 10 data, and grade 4 and grade 5 are not allowed |
| 12 |
Oxidative Induction Time (OIT) |
Standard OIT (min)≥100 |
| High Pressure OIT (min)≥400 |
| 13 |
85℃ thermal aging (Atmospheric Pressure OIT Retention After 90 Day) |
≥55 |
| 14 |
Ultraviolet Irradiation After 1600 Hours, The OIT Retention(%) |
≥50 |
|
(CJ-T234-2006)
| Specification |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
Remark |
| Item |
| Thickness (mm) |
1.00mm |
1.25mm |
1.50mm |
2.00mm |
2.50mm |
3.00mm |
|
| Textured Highth (mm) |
0.25 |
|
| Density (g/c㎡,≥) |
0.94 |
|
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) |
15 |
18 |
22 |
29 |
37 |
44 |
|
| Breaking Strength (N/mm,LD/TD) |
10 |
13 |
16 |
21 |
26 |
32 |
|
| Yeild Elongation Rate (%) |
12 |
|
| Breaking Elongation Rate (%) |
100 |
|
| Rectangular Tear Strength (N) |
125 |
156 |
187 |
249 |
311 |
374 |
|
| Puncture Strength (N) |
267 |
333 |
400 |
534 |
667 |
800 |
|
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) |
300 |
|
| Carbon Black |
| Carbon Black Content(Rang) (%) |
2.0~3.0 |
|
| Carbon Black Dispersion |
Nine of 10 observation area should be grade 1 or grade 2, not more than 1 of grade3 |
|
| Oxidative Induction Time (OIT) |
| Standard OIT (min) |
100 |
|
| High Pressure OIT (min) |
400 |
|
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) |
55 |
|
| 90 days after baking, the hight pressure OIT retention(%) |
80 |
|
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT retention(%) |
50 |
|
| Ultraviolet irradiation after 1600 hours, the high pressure OIT retention(%) |
50 |
|
| -70℃ The Low Temperature Embrittlement Performance mpact |
Pass |
|
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) |
≤1.0X10-13 |
|
| Dimensional Stability |
±2 |
|